The Ion-Exchange Membrane SY-14P series are widely used in chlor-alkali industries, electro-dialysis, recovery of copper from etching solutions, synthesis for gold potassium cyanide , chlorine dioxide, and electrochemical reaction for amino acid. The membrane performs as a conducting separator and solid electrolyte in a variety of electrochemical cells which require the membrane to selectively transport cations across the cell junction.
Membrane SY-14P series are reinforced membranes based on chemically stable perfluorosulfonic acid (PFSA) copolymer. Incorporation of the PTFE mesh reinforcement improves the mechanical property of the composite membrane and allows the membrane to restrict its swelling. The membranes show significant improvements in features such as better resistance to chemical attack and longer operating durability under electrolyzing cell conditions.
Technical Specs of SY14P for chlor-alkali:
Physical and Other Properties |
Values |
Test Method |
Tensile Strength, max., MPa |
50 |
ASTM D882 |
Elongation at break, % |
120 |
ASTM D882 |
Specific Gravity |
1.3 |
体积称重法 |
|
|
|
Other Properties |
Values |
Test Method |
Conductivity, S/cm |
0.083 |
GB/T 20042.3-2009 |
Acid capacity, meq/g |
1.0 |
GB/T 20042.3-2009 |
|
|
|
Hydrolytic Properties |
Values |
Test Method |
Water Content, % |
5.0±3.0 |
ASTMD570 |
Water Uptake, % |
50.0±5.0 |
ASTMD570 |
Thickness Change, |
|
ASTM D 756 |
Linear Expansion, |
|
ASTM D 756 |
Operating Instructions:
1, the voltage: <2.8—3.0v2, the current density: 3.0—6.0 kA/m2
3, or based on the operation condition
Quality of feeding brine:
No. |
Item |
Specifications |
1 |
NaCl |
300--320 g/l |
2 |
Ca+Mg |
<0.02 mg/l |
3 |
Sr |
<0.05 mg/l |
4 |
Ba |
<0.5 mg/l |
5 |
SiO2 |
<2.3 mg/l |
6 |
Al |
<0.1 mg/l |
7 |
I |
<0.2 mg/l |
8 |
Fe |
<0.1 mg/l |
9 |
Ni |
<0.01 mg/l |
10 |
ClO3 |
<15 mg/l |
11 |
SO4 |
<7 g/l |
12 |
TOC |
<10 mg/l |
13 |
SS |
<1 mg/l |
14 |
PH |
9--10 |
Applications:
Chlor-alkali membrane is produced with sacrificial core material, suitable for 30-32% caustic soda production.Chlor-alkali membrane is suitable for running bars with high current density.
Chlor-alkali membrane has higher tolerance to salt water impurities
Size of the Chlor-alkali membrane:
standard size: 1200*1200 mmThe membrane pieces or rolls can be cut to non-standard sizes, please contact our sales staff for details and availability.